PA6 CF10
Comet
Comet
The throughput spool. Industrial parts at 250 mm/s. No new hardware.
Regular price
$105.00
Regular price
Sale price
$105.00
Unit price
$140.00/kg
Shipping calculated at checkout.
Quantity
Couldn't load pickup availability
A carbon-fiber nylon built for volumetric flow. Layer adhesion is maintained at higher print speeds where other filaments show defects, so the printers you already run make more parts per day.
- Prints 50 to 250 mm/s with a hardened steel nozzle
- 27 mm³/s max volumetric flow at 250 mm/s
- 114 MPa tensile strength, 6.7 GPa modulus (XZ, 50 mm/s)
- No new hardware, firmware, or operator training
- Made in the USA
Designed for: Production environments, Rapid field repair, Mission-critical prototyping and tooling.
Provisional datasheet. Tested on Cosmyx NOVA HT, chamber held at 90 °C.
The datasheet, on the page.
Download the datasheet (PDF)| Mechanical, 50 mm/s | XZ / ZX | Method |
|---|---|---|
| Tensile modulus | 6.7 GPa / 3.0 GPa | ISO 527-2 Type 1BA |
| Tensile strength at yield | 114.3 MPa / 49.7 MPa | ISO 527-2 Type 1BA |
| Strain at break | 3.9% / 6.8% | ISO 527-2 Type 1BA |
| Impact, IZOD (measured at 200 mm/s) | 23.3 kJ/m² / 44.0 kJ/m² | ISO 180 |
Provisional datasheet. Tested on Cosmyx NOVA HT, chamber held at 90 °C. Bars cut from printed plates in two orientations.
| Mechanical, 150 mm/s | XZ / ZX | Method |
|---|---|---|
| Tensile modulus | 7.4 GPa / 3.0 GPa | ISO 527-2 Type 1BA |
| Tensile strength at yield | 114.3 MPa / 55.5 MPa | ISO 527-2 Type 1BA |
| Strain at break | 3.4% / 6.0% | ISO 527-2 Type 1BA |
| Mechanical, 250 mm/s | XZ / ZX | Method |
|---|---|---|
| Tensile modulus | 6.7 GPa / 3.9 GPa | ISO 527-2 Type 1BA |
| Tensile strength at yield | 100.3 MPa / 44.4 MPa | ISO 527-2 Type 1BA |
| Strain at break | 4.1% / 3.7% | ISO 527-2 Type 1BA |
| Thermal and physical | Value | Method |
|---|---|---|
| Glass transition, Tg | 60 °C | ISO 11357-2 |
| Melting temperature, Tm | 200 °C | ISO 11357-3 |
| Density | 1.06 g/cm³ | ISO 1183-1 |
| Filament diameter | 1.75 mm ± 0.05 |
| Print settings | Value |
|---|---|
| Nozzle | 280 °C (280 to 310) |
| Bed | 110 °C (90 to 120) |
| Chamber | 90 °C (ambient possible) |
| Nozzle diameter | ≥ 0.6 mm, hardened steel |
| Bed material | Glass, PEI sheet, carbon plate |
| Adhesion | Magigoo PA |
| Drying | 80 °C for 6 to 8 h before printing |
| Annealing | Not required |